供应米兰朵H-105FP/AP高档尼龙鞋材厚版浆透明浆/白胶浆 印花厚版胶浆

H-105FP/AP高档尼龙鞋材厚版浆透明浆/白胶浆  

厚版浆 H-105FP/AP高档尼龙鞋材厚版浆透明浆/白胶浆  性能：

1.外观：H-105FP略显微黄色，H-105AP纯白色

2.配方：有进口Pu树脂与助剂混合合成

3.粘度：145000-155000CPS

4.离子性：非离子

5.贮存期：6个月（常温、密封）

厚版浆  H-105FP/AP高档尼龙鞋材厚版浆透明浆/白胶浆   应用：

1.本产品主要用于梭织布、运动服、尼龙布、涤纶布等立体厚版印花，具有牢固度好、厚度佳、手感柔软、不反粘、立体感强等特点。

2.本产品需要加入配用的助剂1%-2%同时使用

3.本产品一般使用80目120目丝网，根据图案的不同丝网一定要绷紧，这一点相当关键

4.本产品不易塞网，过稠时可加入适量水浆搅拌均匀进行稀释

5.为了保证印制效果，一般根据厚度不同需要印6-8次

6.本产品操作方便，一般建议直接使用平网，不需要制作厚版，在使用厚版网印刷时印完第一次后需待干透后在进行第二次印刷

7.在自然风干48小时后，在过温100-145度左右/8-15秒，过温时尽量将面料过反面（具体温度要根据面料的耐温而做适当的调整）

*以上内容供参考，厂家以自行测试为准*

H-105FP upscale nylon material thick version for transparent paste

H-105AP upscale nylon material thick version of white mortar

Performance:

1 appearance: H-105FP was slightly yellow, H-105AP pure white

2 Formula: imported Pu resin and additives mixed synthetic

3 viscosity: 145000-155000CPS

4: non ion ion

5 storage period: 6 months (room temperature, sealed)

Application:

1 this product is mainly used for woven fabric, sportswear, nylon cloth, polyester cloth and other three-dimensional thick version of printing, has the characteristics ofgood fastness, thickness, soft to the touch, not good anti sticking, three-dimensional sense of strong.

2 this product needs to be added with additives 1%-2% and use

3 this product generally use 80 mesh 120 mesh screen, according to differentscreen pattern must be taut, this point is critical

4 this product is not easy to plug the network, too thick can be added when appropriate slurry mixing dilution

5 in order to ensure the printing effect, general according to the different thicknessneed to print 6-8

6 this product is easy to operate, the general directly using the flat screen, need not produce thick version, in the use of thick version screen printing printing to be dry after the second printing needs first

7 in the natural air dry after 48 hours, the over temperature 100-145 degrees /8-15 seconds, over temperature as the fabric is negative (specific temperature to be adjusted according to the temperature resistant fabric)

* the above for reference, manufacturers to test for quasi *